ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu | |
RIALACHA GB/T | 0.04-0.14 | 6.5-8.0 | 0.65-1.0 | 18.5-22.0 | 8.0-10.7 | 0.75 | 0. 03 | 0. 03 | 0.75 | |
RIALACHA AWS | - | - | - | - | - | - | - | - | - | |
LUACH SAMPLACH | 0. 071 | 6.73 | 0.7 | 18.83 | 8.96 | 0. 01 | 0. 014 | 0. 012 | 0. 01 |
MAOIN MEICNIÚIL:
MAOINE | YIELD STRENGTH(MPa) | NEART BREISE(MPa) | LUACH IMAPACT J/ ℃ | ELONGATION(%) | ||||
RIALACHA GB/T | - | - | - | - | ||||
RIALACHA AWS | - | - | - | - | ||||
LUACH SAMPLACH | - | 630 | - | 39 |
Paraiméadair Táthú MOLTA:
SONRAÍOCHTAÍ TÉIMÉADAIR(mm) | 0.8 | 1.0 | 1.2 | ||||
LEICTREACHAS (Amp) | H/W | 70-150 | 100-200 | 140-220 | |||
O/W | 50-120 | 80-150 | 120-180 |
Peculiarity

Is é an príomh-chomhpháirt 18% Cr-8% Ni-6%Mn.
Beathú sreang réidh, stua cobhsaí, foirmiú álainn, sreabhadh maith d'iarann leáite, níos lú splancscáileán, le feidhmíocht phróiseas táthú den scoth.


Tá dea-airíonna meicniúla ag miotail leáite.
Taispeáin sonraí


Cobhsaíocht stua
Cruth álainn
Maidir linne

Taispeáint fioor mhonarcha




Cás iarratais


Harbin leictreacha trí dhoras CMT
Tionscadal píblíne onnmhairithe Tangshan LNG
Lámhach monarcha fíor

COMHPHÁIRT CHEIMICEACH:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu | |
RIALACHA GB/T | 0.04-0.14 | 6.5-8.0 | 0.65-1.0 | 18.5-22.0 | 8.0-10.7 | 0.75 | 0. 03 | 0. 03 | 0.75 | |
RIALACHA AWS | - | - | - | - | - | - | - | - | - | |
LUACH SAMPLACH | 0. 071 | 6.73 | 0.7 | 18.83 | 8.96 | 0. 01 | 0. 014 | 0. 012 | 0. 01 |
MAOIN MEICNIÚIL:
MAOINE | YIELD STRENGTH(MPa) | NEART BREISE(MPa) | LUACH IMAPACT J/ ℃ | ELONGATION(%) | ||||
RIALACHA GB/T | - | - | - | - | ||||
RIALACHA AWS | - | - | - | - | ||||
LUACH SAMPLACH | - | 630 | - | 39 |
Paraiméadair Táthú MOLTA:
SONRAÍOCHTAÍ TÉIMÉADAIR(mm) | 0.8 | 1.0 | 1.2 | ||||
LEICTREACHAS (Amp) | H/W | 70-150 | 100-200 | 140-220 | |||
O/W | 50-120 | 80-150 | 120-180 |